Alternative Loctite 416 Super Bonder Instant Adhesive


         Alternative Loctite 416 Super Bonder Instant Adhesive

                                                       from Tina(hengying@cnhybond.com   0086-18927302778  Skype:hengying11)



Product Description 
CNHYbond 416 is a general purpose cyanoacrylate instant adhesive. Medium  viscosity ,bonding rubber,metal and plastics, gap fill up to 0.1mm

Product Characteristics 
Technology :                      Cyanoacrylate 
Chemiacl Type:                    Ethyl cyanoacrylate
Appearance(uncured):               Transparent colorless liquid
Components:                      one part-require no mixing
Viscosity,Brookfield-LVF,25℃1:   1000-1600cps
         Spindle 1,speed 30 rpm
Cure:                             Humidity
Application:                       Bonding
Key substrates:                     Metals, plastics and Rubber
Specific Gravity@25℃:             1.05

Typical Curing Performance
Under normal conditions, the atmospheric moisture initiates the curing process. Although full functional strength is developed in a relatively short time, curing continues for at least 24 hours before full chemical/solvent resistance is developed.

Cure Speed vs. Substrate
The rate of cure will depend on the substrate used. The table
below shows the fixture time achieved on different materials
at 22 °C / 50 % relative humidity. This is defined as the time to
develop a shear strength of 0.1 N/mm².
Fixture Time, ISO 4587, seconds:
Mild Steel (degreased) 20 to 40
Aluminum (degreased) 10to 25
Zinc Dichromate 40 to 90
Neoprene <5
Rubber, Nitrile <5
ABS 10 to 40
PVC 20 to 50
Polycarbonate 20 to 70
Phenolic 10 to 40

Cure Speed vs. Bond Gap
The rate of cure will depend on the bondline gap. Thin bond lines result in high cure speeds, increasing the bond gap will decrease the rate of cure.

Cure Speed vs. Humidity
The rate of cure will depend on the ambient relative humidity. Higher relative humidity levels result in more rapid speed of cure.

Cure Speed vs. Activator
Where cure speed is unacceptably long due to large gaps, applying activator to the surface will improve cure speed. However, this can reduce ultimate strength of the bond and  herefore  testing is recommended to confirm effect.

Directions for use:
(1). Bond areas should be clean and free from grease. Clean all surfaces with a CNHYBOND cleaning solvent and allow to dry.
(2).CN HYBOND Primer may be applied to the bond area. Avoid applying  excess Primer. Allow the Primer to dry.
(3). HYBOND Activator may be used if necessary. Apply the  CNHYBOND Activator to one bond surface (do not apply activator  to the primed surface where Primer is also used). Allow the Activator to dry 
(4). Apply adhesive to one of the bond surfaces (do not apply the adhesive to the activated surface). Do not use items like tissue or a brush to spread the adhesive. Assemble the parts within a few seconds. The parts should be accurately located, as the short fixture time leaves little opportunity for adjustment.
(5).CNHYBOND Activator can be used to cure fillets of product outside the bond area. Spray or drop the activator on the excess product.
(6). Bonds should be held fixed or clamped until adhesive has fixtured.
(7). Product should be allowed to develop full strength before subjecting to any service loads (typically 24 to 72 hours after assembly, depending on bond gap, materials and ambient conditions).

Storage
Store product in the unopened container in a dry location. Storage information may be indicated on the product container
labeling.
Optimal Storage: 2 °C to 8 °C. Storage below 2 °C or greater than 8 °C can adversely affect product properties. Material removed from containers may be contaminated during
use. Do not return product to the original container. Heng ying Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.

Sunday, April 26, 2015

Alternative Loctite 495 Ethyl Instant Adhesive


             Alternative Loctite 495 Ethyl Instant Adhesive

                                                                   from Tina(hengying@cnhybond.com  0086-18927302778  Skype:hengying11)




1. Product Description 
HYBOND 495 is a general purpose, medium viscosity cyanoacrylate instant adhesive.
Application: bonding rubber, metal and plastics, max. gap fill up to 0.1mm


2. Product Characteristics 
Technology
Cyanoacrylate 

Chemical Type
  Ethyl cyanoacrylate
Appearance (uncured)
  Transparent colorless liquid

Components
one part-require no mixing

Viscosity,Brookfield-LVF,25℃1
             Spindle 1, speed 30 rpm
40-60cps
Cure
Humidity

Application
Bonding

Key bstrates
Metals, plastics and Elastomers

Specific Gravity@25℃:
     1.5

3. Typical Curing Performance 
Under normal conditions, the atmospheric moisture initiates the curing process. Although full functional strength is developed in a relatively short time, curing continues for at least 24 hours before full chemical/solvent resistance is developed.

4. Cure Speed vs. Substrate
The rate of cure will depend on the substrate used. The table below shows the fixture time achieved on different materials at 22 °C / 50 % relative humidity. This is defined as the time to develop shear strength of 0.1 N/mm².
Fixture Time, ISO 4587, seconds:
Mild Steel (degreased)
10 to 30
Aluminum(degreased)
5 to 15
Zinc dichromate
30 to 90
Neoprene
<5
Rubber, nitrile
<5
ABS
10 to 30
PVC
3 to 10
Polycarbonate
20 to 60
Phenolic
5 to 20

5. Cure Speed vs. Bond Gap
The rate of cure will depend on the bondline gap. Thin bond lines result in high cure speeds, increasing the bond gap will decrease the rate of cure.

6. Cure Speed vs. Humidity
The rate of cure will depend on the ambient relative humidity. Higher relative humidity levels result in more rapid speed of cure.

7. Cure Speed vs. Activator
Where cure speed is unacceptably long due to large gaps, applying activator to the surface will improve cure speed. However, it can reduce ultimate strength of the bond effect.

8. Directions for use:
(1). Bond areas should be clean and free from grease. Clean all surfaces with a HYBOND cleaning solvent and allow to be dried.
(2). HYBOND Primer may be applied to the bond area. Avoid applying excess Primer. Allow the Primer to dry.
(3). HYBOND Activator may be used if necessary. Apply HYBOND Activator to one bond surface (do not apply activator to the primed surface where Primer is also used). Allow the Activator to dry 
(4). Apply adhesive to one of the bond surfaces (do not apply the adhesive to the activated surface). Do not use items like tissue or a brush to spread the adhesive. Assemble the parts within a few seconds. The parts should be accurately located, as the short fixture time leaves little opportunity for adjustment.
(5). HYBOND Activator can be used to cure fillets of product outside the bond area. Spray or drop the activator on the excess product.
(6). Bonds should be held fixed or clamped until adhesive has fixtured.
(7). Product should be allowed to develop full strength before subjecting to any service loads (typically 24 to 72 hours after assembly, depending on bond gap, materials and ambient conditions).

9.Storage
Store product in the unopened container in a dry location, storage instruction is shown on the label of bottle

Optimal Storage: 2 °C to 8 °C. Storage below 2 °C or greater than 8 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container. Heng ying Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.

Wednesday, April 22, 2015

Alternative Loctite496 Super Bonder Instant Adhesive


                Alternative Loctite496 Super Bonder Instant Adhesive 

                                             from Shirley(hengying@cnhybond.com  0086-18927302778  Skype:hengying11)



Product Description 
HYBOND 496 is a general purpose cyanoacrylate instant adhesive. It is particularly suited to bonding of metal substrates

Product Characteristics 
Technology
Cyanoacrylate 

Chemical Type
Ethyl cyanoacrylate
Appearance (uncured)
Transparent colorless liquid

Components
one part-require no mixing

Viscosity,Brookfield-LVF,25℃1
             Spindle 1, speed 30 rpm
40-60cps
Cure
Humidity

Application
Bonding

Key substrates
Metals, plastics and Elastomers

Specific Gravity@25℃:
     1.1

Typical Curing Performance 

Under normal conditions, the atmospheric moisture initiates the curing process. Although full functional strength is developed in a relatively short time, curing continues for at least 24 hours before full chemical/solvent resistance is developed.

Cure Speed vs. Substrate
The rate of cure will depend on the substrate used. The table below shows the fixture time achieved on different materials at 22 °C / 50 % relative humidity. This is defined as the time to develop shear strength of 0.1 N/mm².
Fixture Time, seconds:
Mild Steel (degreased)
20 to 40
Aluminum
30 to 60
Zinc dichromate
30 to 60
Neoprene
<10
Rubber, nitrile
<10
ABS
10 to 30
PVC
30 to 70
Polycarbonate
20 to 70
Phenolic
10 to 30


Cure Speed vs. Bond Gap
The rate of cure will depend on the bondline gap. Thin bond lines result in high cure speeds, increasing the bond gap will decrease the rate of cure.

Cure Speed vs. Humidity
The rate of cure will depend on the ambient relative humidity. Higher relative humidity levels result in more rapid speed of cure.

Cure Speed vs. Activator
Where cure speed is unacceptably long due to large gaps, applying activator to the surface will improve cure speed. However, it can reduce ultimate strength of the bond effect.

Directions for use:
(1). Bond areas should be clean and free from grease. Clean all surfaces with a HYBOND cleaning solvent and allow to be dried.
(2). HYBOND Primer may be applied to the bond area. Avoid applying excess Primer. Allow the Primer to dry.
(3). HYBOND Activator may be used if necessary. Apply HYBOND Activator to one bond surface (do not apply activator to the primed surface where Primer is also used). Allow the Activator to dry 
(4). Apply adhesive to one of the bond surfaces (do not apply the adhesive to the activated surface). Do not use items like tissue or a brush to spread the adhesive. Assemble the parts within a few seconds. The parts should be accurately located, as the short fixture time leaves little opportunity for adjustment.
(5). HYBOND Activator can be used to cure fillets of product outside the bond area. Spray or drop the activator on the excess product.
(6). Bonds should be held fixed or clamped until adhesive has fixtured.
(7). Product should be allowed to develop full strength before subjecting to any service loads (typically 24 to 72 hours after assembly, depending on bond gap, materials and ambient conditions).

Storage
Store product in the unopened container in a dry location, storage instruction is shown on the label of bottle

Optimal Storage: 2 °C to 8 °C. Storage below 2 °C or greater than 8 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container. Heng ying Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.

Friday, April 17, 2015

Loctite 770 Quality Primer for Instant Glue


             Loctite 770 Quality Primer for Instant Glue 

                                                                  from Tina(hengying@cnhybond.com    0086-18927302778  Skype:hengying11)



Product Description 
Characteristics:
Technology :                         Primer - Cyanoacrylate
Chemical Type:                       Aliphatic amine
Solvent:                            n-Heptane
Active Ingredient  Concentration, %:       0.08 to 0.12LMS
Appearance :                        Clear colorless liquidLMSS
Viscosity :                           Very low
Cure:                              Not applicable
Application:CA Surface Primer

HYBOND770 Primer is used to make polyolefin and other low energy surfaces suitable for bonding with hybond cyanoacrylate adhesives. On such treated surfaces the cured performance of cyanoacrylate adhesives is generally similar to that described in the TDS for the relevant adhesive. It is only recommended for difficult to bond substrates which include polyethylene, polypropylene, polytetrafluoroethylene (PTFE) and thermoplastic rubber materials. It is not recommended in assemblies where high peel strength is required. HYBOND770 is also suitable for use in the assembly of disposable medical devices.
.
Typical Properties
Specific Gravity @ 25 °C:                        0.68
Viscosity @ 20 °C, mPa·s (cP) :                  1.25
Drying Time @ 20 °C,                           seconds ≤30
On Part Life,                                    hours ≤8

Typical Performance 
Fixture time and cure speed achieved as a result of using HYBOND 770 primer depend on the adhesive used and the substrate bonded.

Effect on Cure Speed of Cyanoacrylate Adhesives
HYBOND 770Primer also behaves as an activator and accelerates the cure speed of cyanoacrylate adhesives.Fixturing time on most primed substrates is less than 5 seconds but 24 hours at room temperature (22 °C) should be allowed for adhesive to develop maximum bond strength

Effect on Cured Properties of Cyanoacrylate Adhesives
Products 406, 496 and 868 are based on ethyl, methyl and ß-Methoxyethyl esters respectively. Other liquid  products based on these esters will behave in a similar fashion to these examples. HYBOND 770 Primer is not recommended for use with gel products.

Directions for use
Primer may be applied by spraying, brushing or dipping at ambient temperature. Excess primer should be avoided. If polyolefin and more active or easier to bond materials are involved, apply the primer to the polyolefin only.

Handling precautions
Primer must be handled in a manner applicable to highly flammable materials and in compliance with relevant local regulations. The solvent can affect certain plastics or coatings. It is recommended to check all surfaces for compatibility before.

Storage
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.
Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container.HYBOND Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.

Tuesday, April 14, 2015

CA Adhesive Cure Accelerator 7452


                  CA Adhesive Cure Accelerator 7452

                                                                     from Tina(hengying@cnhybond.com  0086-18927302778  Skype:hengying11)


PRODUCT DESCRIPTION
Characteristics:
Technology: Cyanoacrylate Activator
Solvent: Acetone
Active Ingredient Concentration, %              0.8 to 0.95LMS
Appearance Transparent colorless to slightly:    amber liquidLMS
Viscosity: Very low
Cure: Not applicable
Application : CA adhesive cure accelerator

HYBOND 7452™ is used where increased cure speed of cyanoacrylate adhesives is required. It can be
either pre- or post-applied to the bond. The product is especially suited for post-application on cyanoacrylate adhesive to ensure rapid fixturing. Typical applications include securing wires or coils to PCBs, tamper-proofing adjustable components, mounting stand-offs, edge guides and board stiffeners.

TYPICAL PROPERTIES
Specific Gravity @ 25 °C 0.79
Viscosity @ 20 °C, mPa·s (cP) 0.3 to 0.5
Drying Time @ 20 °C,     seconds ≤30
On Part Life             , minutes ≤1

TYPICAL PERFORMANCE
Fixture time and cure speed achieved as a result of using 7452 Activator depend on the adhesive used and the substrate bonded.
Fixture Time, ISO 4587, seconds:Steel (grit blasted) using  hybond ® 495™,two side activation
≤10LMS
(Fixture time is defined as the time to develop a shear strength
of 0.1 N/mm²)

Handling precautions
Activator must be handled in a manner applicable to highly flammable materials and in compliance with relevant local regulations.The solvent can affect certain plastics or coatings. It is ecommended to check all surfaces for compatibility before use.

Directions for use

(1)Post Activation
1. Apply cyanoacrylate to the parts to be bonded or fixed.
2. Apply Activator over all exposed cyanoacrylate adhesive by spray or drop. (Typically use one drop of activator per drop of exposed adhesive).

(2).Surface Activation
1. Apply one coating of Activator to the area to be bonded by spray, brush or dipping. Contaminated surfaces may need special cleaning or degreasing prior to activation to remove any soluble contamination.
2. Allow HYBOND 7452™ to fully evaporate from parts prior to bonding to avoid solvent entrapment within the bond joint.
3. Apply the cyanoacrylate product immediately after drying or not more than 45seconds thereafter.
4. Activator can be re-applied if necessary if there is a delay of more than 45seconds between original activator and adhesive application.

Storage
This activator is classified as HIGHLY FLAMMABLE and must be stored in an appropriate manner in compliance with relevant regulations. Do not store near oxidising agents or combustible materials. The product is light sensitve and accordingly, translucent containers should be kept in a dark place when not in use. Store product in the unopened container in a dry location. Storage information may also be indicated on the product container labelling.
Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties
Material removed from containers may be contaminated during use. Do not return product to the original container. It cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.